Silica bricks are used more in glass melting furnaces, and the main component is silica (SiO2). The silica brick used in the glass melting furnace requires a SiO2 content of 94% or more, a maximum use temperature of about 1600 to 1650 ° C, and a density of 1.8 to 1.95 g/cm 3 . The apparent porosity requirement is less than 22%, the larger the porosity, the worse the quality of the silica brick.

"/>

亚洲日韩成人av无码网站,色翁荡熄又大又硬又粗又动态图,无码aⅴ精品一区二区三区,国产精品久久久久免费a∨

Outerwear of Glass Melting Furnace: Analysis of Common Refractory Materials in Glass Kiln and Their Characteristics

Time:2019-09-20 10:40:18Browse volume:

Silica brick for glass kiln


Silica bricks are used more in glass melting furnaces, and the main component is silica (SiO2). The silica brick used in the glass melting furnace requires a SiO2 content of 94% or more, a maximum use temperature of about 1600 to 1650 ° C, and a density of 1.8 to 1.95 g/cm 3 . The apparent porosity requirement is less than 22%, the larger the porosity, the worse the quality of the silica brick. The appearance of silica brick is mostly white crystal, and the microscopic composition is the crystal of tridymite. Because of the transformation of crystals at high temperature, the volume expansion, especially at 180-270 ° C and 573 ° C, the crystal transformation is more In order to be fierce, in the process of roasting kiln and cold repair, it is necessary to take appropriate measures such as elastic brace to adapt to the crystallization transformation of silica brick. Silicon brick masonry should have expansion joints.


Silica bricks have a working temperature of about 200 °C higher than that of clay bricks, but they have poor erosion resistance to glass liquid and alkaline flying materials, so they are used to build large structures such as large concrete, chest walls and small furnaces. In the masonry, high-silicon refractory mud or silicon brick powder and other materials close to the silica brick composition should be used as the cementing material.


Clay brick for glass kiln


The main components of clay bricks are Al2O3 and SiO2. The content of Al2O3 is between 30% and 45%, the SiO3 is between 51% and 66%, the density is 1.7~2.4g/cm3, and the apparent porosity is 12%~21%. The use temperature is 1350~1500 °C. In the glass industry, clay bricks are used to build the bottom of the kiln. The wall of the working part and the passage, the wall of the regenerator, the raft, the lower lattice brick and the flue. As the temperature rises, the clay bricks expand in volume. When the temperature exceeds 1450 ° C, the volume shrinks.


High alumina brick


The main component of high alumina bricks is also SiO2 and Al2O3, but Al2O3 should be greater than 46%. It is made of corundum, high alumina bauxite or sillimanite mineral (Al2O3-SiO2). The density is 2.3~3.0g/cm3, the apparent porosity is about 18%~23%, and the maximum use temperature is 1500~1650°C. When the porosity of the high alumina brick is low, the corrosion resistance is good. High-aluminum bricks can be used to build cooling pool walls, regenerators, regenerator walls, etc.


Mullite brick


The main component of mullite bricks is Al2O3, which is about 75%. Because it is mainly mullite crystal, it is called mullite brick. The density is 2.7 - 3 2g / cm3, the open porosity is 1% - 12%, and the maximum operating temperature is 1500 ~ 1700 °C. Sintered mullite is mainly used to build regenerator walls.


The fused mullite is mainly used for laying pool walls, observation holes, wall sills, and the like.


Electric melting zirconium corundum brick


The fused zirconia corundum brick is also called white iron brick, and the fused zirconium corundum brick is generally classified into 33%, 36%, and 41% according to the content of zirconium. Zirconium corundum brick used in the glass industry contains 50%~70% Al2O3, 20%~40% ZrO2, density 3.4~4.0g/cm3, apparent porosity 1%~10%, maximum temperature is about 1700°C, including The fused zirconium corundum brick with 33% and 36% zirconium is used for masonry kiln pool wall, flame space chest wall, small furnace squirting port, small furnace flat shovel, small furnace shovel, tongue sputum, etc. The % fused corundum brick is used to build the corners of the pool wall, fluid holes and other glass to violently eroded the most severe parts of the eclipse. This material is the most widely used fused cast refractory in the glass industry.


Fused alumina brick


It mainly refers to fused α, β corundum, fused β corundum fused cast refractory bricks, mainly composed of 92%~94% Al2O3 corundum crystal phase, density 2.9~3.05g/cm3, apparent porosity 1%~10%, highest The use temperature is around 1700 °C.


The fused alumina has excellent anti-glass dialysis ability and hardly pollutes the glass. It is widely used in the glass wall of the working chamber of the glass melting furnace, the bottom of the tank, the flow channel, the channel wall of the working section, the bottom of the material channel, etc., and the parts which are not required to be contaminated by refractory materials.


Quartz brick


The main component of quartz brick is SiO2, which contains up to 99%, density of 1.9~2g/cm3, refractoriness of 1650°C, working temperature of about 1600°C, acid corrosion resistance, used to build the wall of acid boron glass. Flame space thermocouple hole bricks, etc.


Alkaline refractory


Alkaline refractory materials mainly refer to magnesia bricks, aluminum-magnesia bricks, magnesia-chrome bricks, and forsterite bricks. Its performance is corrosion resistance to alkaline materials, and the refractoriness is 1900-2000 °C. It is widely used in the upper wall of the regenerator of the glass melting furnace, the regenerator chamber, the structure of the body, and the structure of the small furnace.


Glass kiln insulation brick


The glass melting furnace has a large heat dissipation area and low thermal efficiency. In order to save energy and reduce consumption, it is necessary to use a large amount of thermal insulation material for comprehensive thermal insulation. In particular, the pool wall, the bottom of the pool, the concrete, and the wall of the regenerator, the melting section, and the working part are insulated to reduce heat dissipation. The insulating brick has a large porosity and a very low mass, and the density does not exceed 1.3 g/cm3. Since the heat transfer performance of the air is poor, the heat insulating brick having a large porosity has an adiabatic effect. Its heat transfer coefficient is 2~3 times lower than that of general refractory materials, so the larger the porosity, the better the heat preservation effect. There are many different types of insulation bricks, such as clay insulation bricks, silicon insulation bricks, and high aluminum insulation bricks.


亚洲av无码片在线观看| 欧美牲交a欧美牲交| 国产69久久精品成人看| 久久精品国产大片免费观看| 国产精品国色综合久久| 亚洲男人第一无码av网站| 无码h黄动漫在线播放网站| 久青草影院在线观看国产| 国产啪亚洲国产精品无码| 国产精品99久久久久久www| 国产精品h片在线播放| 国产精品久久久久久52avav| 国产丝袜美女一区二区三区| 国产sp调教打屁股视频网站| 中文字幕av一区二区三区人妻少妇| 亚欧中文字幕久久精品无码| 麻豆国产av丝袜白领传媒| 日本午夜精品一区二区三区电影| 欧美成人精品高清视频在线观看| 性生交大全免费看| 成人免费无码视频在线网站| 亚洲乱亚洲乱妇| 男女猛烈无遮挡免费视频| 精品国产v无码大片在线观看| 亚洲av无码精品色午夜| 中文在线最新版天堂| 午夜dv内射一区区| 色婷婷综合久久久久中文一区二区| 午夜福利视频合集1000| 老司机在线ae85| 欧美白人战黑吊| 亚洲av无码成人网站在线观看| 久久午夜无码鲁丝片午夜精品| 亚洲av无码一区二区三区在线| 久久综合噜噜激激的五月天| 精品爆乳一区二区三区无码av| 寂寞少妇做spa按摩无码| 日本熟妇浓毛| 国产精品国色综合久久| 国产精品久久久久久人妻精品| 香蕉久久av一区二区三区|